| http://www.w3.org/ns/prov#value | - Their performance properties of orientation (except for sample 20 which had a poor orientation of 38 feet/minute) and % shrink were substantially similar to those of LLDPE control samples 2A-2D, but their abuse resistance (except for sample 20 which had a Carson Dart Drop of 35.6 cm) was not as high as that of 2A-2D. In fact, for sample 28, abuse resistance was a poor 15.2 cm.
|