| http://www.w3.org/ns/prov#value | - Therefore, dislocations mostly appeared at interface and inside the W layers as observed in Figure 3.As the individual layer thickness of Al was increased to 5???nm, the energy derived from lattice fit dropped below the volume energy of the strained Al film.
|